Inslogic PA6-GF25 Filament (Nylon 6 Reinforced with 25% Glass Fiber)
High-strength, heat-resistant engineering material (210°C) for FDM 3D printers.
Product Description
Elevate your 3D printing to industrial standards with Inslogic PA6-GF25. Inslogic PA6-GF25 is an engineering-grade filament designed for ultimate strength, using a Nylon 6 (PA6) base reinforced with 25% glass fiber. The result is a material with significantly higher dimensional stability and stiffness than standard nylon.
Weight 1 KG
Why choose Inslogic PA6-GF25?
-
High heat resistance: With a high Heat Deflection Temperature (HDT) of up to 210°C , printed objects can be used in high-temperature environments without deformation.
-
Excellent mechanical strength: With 25% glass fiber reinforcement, the material achieves a tensile strength of up to 125 MPa and excellent flexural strength, making it suitable for heavy-duty applications.
-
Accuracy and ease of printing: Designed to minimize warping issues commonly found in typical nylon materials, it provides strong layer adhesion, resulting in highly accurate prints.
-
Chemical and wear resistant: Resistant to abrasion and many types of chemicals, making it suitable for jigs, fixtures, or machine parts.
Proper usage:
-
Automotive and engineering parts
-
Structures that must withstand high compressive or tensile forces.
-
Equipment requiring resistance to heat and chemicals.
-
Functional prototypes and end-use parts.
Technical Specifications
-
Material: 25% Glass Fiber Reinforced Nylon 6
-
Printing temperature (Nozzle Temp): 270 - 290 °C
-
Bed temperature: 50 - 70 °C
-
Printing speed: 50 - 120 mm/s
-
Tensile Strength: 125 MPa
-
Heat resistance temperature (HDT): 210 °C (at 0.45 MPa)
-
Diameter: 1.75 mm (±0.03 mm)
-
Additional recommendation: Hardened steel nozzles should be used because glass fibers are highly corrosive.
Additional advice: Because this material is hygroscopic, please specify on the product page regarding drying the filament at 80-100°C for 4-6 hours before printing for best results.